Chrome Alloyed Ball Mill Liner Plates powder grinding mill Liner Plate; ball mill machine spare parts
Chrome alloyed casting iron is divided into three types: high chrome alloyed casting iron(with the chromium content at 8-26%, the carbon content at 2.0-3.6%), medium chrome alloyed casting iron(with the chromium content at 4-6%, the carbon content at 2.0-3.2%), low chrome alloyed casting iron(with the chromium content at 1-3%, the carbon content at 2.1-3.6%). Its distinctive features is that the M7C3 type eutectic carbide micro hardness is HV1300-1800. The eutectic carbide is distributed on the base, martensite (the most hard metal matrix organization), in discontinuous network and isolation, which reduces the fragmentation of the matrix effect. As a result, the high chromium ball mill liner has high strength, strong toughness and good wear resistance performance, which represents the highest level of metal wear resistant materials.
Spec Available
| Name | Chemical Elements(%) | |||||||
| C | Si | Mn | Cr | Mo | Cu | P | S | |
|
High Chrome Alloyed Liner |
2.0-3.6 | 0-1.2 | 0-2.0 | 8-26 | ≤3.0 | ≤1.2 | ≤0.06 | ≤0.06 |
|
Middle Chrome Alloyed Liner |
2.0-3.3 | 0-1.2 | 0-2.0 | 3-8 | ≤3.0 | ≤1.2 | ≤0.06 | ≤0.06 |
|
Low Chrome Alloyed Liner |
2.1-3.6 | 0-1.5 | 0-2.0 | 1-3 | 0-1.0 | ≤1.2 | ≤0.06 | ≤0.06 |
Physical Property & Microstructure
| Name | Surface(HRC) | Ak(J/cm2) | Microstructure |
|
High Chrome Alloyed Liner |
≥58 | ≥3.5 | M+C+A |
|
Middle Chrome Alloyed Liner |
≥48 | ≥10 | M+C |
|
Low Chrome AlloyedLiner |
≥45 | ≥15 | M+C+P |
| Martensite Carbide Austenite Pearlite | |||
Specification
| Size | Hole Dia.(mm) | Liner Length(mm) | ||
| ≤40 | ≥40 | ≤250 | ≥250 | |
| Tolerance |
+2 0 |
+3 0 |
+2 | +3 |